5mm 100mm Duplex 2205 S32205 Plat Duplex Plat Baja S31803 2B 1D Permukaan

Sertifikasi
CINA JIANGSU MITTEL STEEL INDUSTRIAL LIMITED Sertifikasi
CINA JIANGSU MITTEL STEEL INDUSTRIAL LIMITED Sertifikasi
Ulasan pelanggan
this is the second order l buy this company ,quality is very good ,same as europure quality .we will go on ccooperate with this company .

—— Andrew Greg - Turkey

200 ton Stainless steel sheet is arrived on 10th Oct 2014 , the quality is very good.,deliver time is very fast It's very lucky we find this factory

—— Mechile Kilar Chard - Brazial

We Have Cooperate With this Factory Many Years , Everything Goes Very Well.l Like This Factory !

—— Tony Hilton - Poland

This is Our Thrid Time Buy from Mittel,Quality is Very Goods ,We Are Glad to Find This Reliable Factory

—— Natalya Ugay-Russia

Quality is very good and delivery time very fast ,we want to do long terms business with this company

—— Pongpol Pluemsati-Thailand

I 'm Online Chat Now

5mm 100mm Duplex 2205 S32205 Plat Duplex Plat Baja S31803 2B 1D Permukaan

5mm   100mm Duplex 2205 S32205 Plat Duplex Plat Baja S31803 2B 1D Permukaan
5mm   100mm Duplex 2205 S32205 Plat Duplex Plat Baja S31803 2B 1D Permukaan 5mm   100mm Duplex 2205 S32205 Plat Duplex Plat Baja S31803 2B 1D Permukaan 5mm   100mm Duplex 2205 S32205 Plat Duplex Plat Baja S31803 2B 1D Permukaan

Gambar besar :  5mm 100mm Duplex 2205 S32205 Plat Duplex Plat Baja S31803 2B 1D Permukaan

Detail produk:
Tempat asal: China(Mainland)
Nama merek: AUTO KUMPO / TISCO / BAOSTEEL
Sertifikasi: SGS,BV
Nomor model: 2205
Syarat-syarat pembayaran & pengiriman:
Kuantitas min Order: 1 TON
Harga: 4000-5500 USD/Ton
Kemasan rincian: standar ekspor kemasan layak laut atau seperti yang dipersyaratkan
Waktu pengiriman: 5-10 hari sesuai dengan kuantitas
Syarat-syarat pembayaran: L/C, T/T, Western Union
Menyediakan kemampuan: 15000Tons

5mm 100mm Duplex 2205 S32205 Plat Duplex Plat Baja S31803 2B 1D Permukaan

Deskripsi
jenis perusahaan: agen TISCO Teknologi Pemrosesan: Digulung Dingin
Kelas: S31803 s32205 2507 s32750 Permukaan: 2B BA NO.4 Cermin 8K
Standar: ASTM AISI GB DIN JIS EN sertifikat: SGS/BV
Cahaya Tinggi:

pelat baja stainless dupleks

,

baja duplex super

5mm 100mm Duplex 2205 Plat, Duplex Steel Pipe S31803 2B 1D permukaan

Dibandingkan dengan baja tahan karat austenit biasa, baja 2205 memiliki koefisien ekspansi termal yang lebih rendah tetapi konduktivitas termal yang lebih tinggi

2205 mengkarakterisasi

  • ketahanan yang baik terhadap retakan korosi tegangan.

  • ketahanan tinggi terhadap korosi umum, celah dan lubang;

  • ketahanan tinggi terhadap korosi erosi dan kelelahan korosi;

  • kekuatan mekanik yang tinggi;

  • sifat fisik yang menarik;

  • kemampuan las yang baik

2205spesifikasi

1) Ketebalan: 5mm 100mm
2)Lebar: 1,5 meter, 2 meter, 2,5 meter, 3 meter
3) Panjang: Hingga 12 meter

4) Tingkat:LDX2101,2304,2205,2507, dll

2205 aplikasi

Kapal tekanan, tangki penyimpanan tekanan tinggi, pipa tekanan tinggi,

penukar panas (industri pengolahan kimia), pipa minyak dan gas,

penukar panas, pipa, pengolahan air limbah, industri pulp dan kertas

klasifikasi, peralatan pemutih, sistem penyimpanan dan pemrosesan,

korosi kekuatan tinggi di bawah poros putar, roll press, bilah, impeller, kapal

atau kotak kargo truk, peralatan pengolahan makanan, peralatan lingkungan laut.

Aplikasi

Kapal tekanan, tangki, pipa, dan penukar panas di industri pengolahan kimia
Pipa, tabung, dan penukar panas untuk penanganan gas dan minyak
Sistem pembersih limbah
Digester industri pulp dan kertas, peralatan pemutih, dan sistem penanganan stok
Rotor, kipas angin, poros, dan gulung pers yang membutuhkan kekuatan gabungan dan ketahanan korosi
Tangki kargo untuk kapal dan truk
Peralatan pengolahan makanan
Pabrik biofuel


------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------

Standar
ASTM/ASME...........A240 UNS S32205/S31803
EURONORM........1.4462 X2CrNiMoN 22.5.3
AFNOR Z3 CrNi 22,05 AZ
DIN...........................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................................4462

------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------

Ketahanan Korosi
Korosi Umum
Karena kandungan kromium (22%), molibdenum (3%) dan nitrogen (0,18%) yang tinggi, sifat ketahanan korosi 2205 lebih baik daripada 316L atau 317L di sebagian besar lingkungan.

Ketahanan Korosi Tekanan
Mikrostruktur dupleks diketahui meningkatkan ketahanan retak korosi stres dari stainless steel.

Kerusakan korosi tekanan klorida dari stainless steel austenitic dapat terjadi ketika kondisi suhu, tekanan tarik, oksigen, dan klorida yang diperlukan ada.Karena kondisi ini tidak mudah dikendalikan, retakan korosi stres sering menjadi penghalang untuk menggunakan 304L, 316L, atau 317L.

Ketahanan terhadap korosi dan kelelahan
Alloy 2205 menggabungkan kekuatan tinggi dan ketahanan korosi yang tinggi untuk menghasilkan kekuatan kelelahan korosi yang tinggi.Aplikasi di mana peralatan pengolahan tunduk pada lingkungan yang sangat korosif dan beban siklus dapat mendapatkan keuntungan dari sifat 2205.

------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------

Analisis Kimia
Nilai tipikal (% berat)

C Cr Ni Mo N lainnya
0.020 22.1 5.6 3.1 0.18 S=0.001
PREN = [Cr%] = 3,3 [Mo%] = 16 [N%] ≥ 34

------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------

Sifat Mekanis
Sifat Mekanis pada Suhu Kamar

ASTM A 240 Tipikal
Kekuatan hasil 0,2%, ksi 65 min. 74
Kekuatan tarik, ksi 90 menit 105
Perpanjangan % 25 min. 30
Kekerasan HB 293 maksimal 256

------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------

Struktur
Analisis kimia 2205 dioptimalkan untuk mendapatkan mikrostruktur 50 a/ 50 g yang khas setelah perawatan penggilingan larutan pada 1900/1922F (1040/1080C).

Pengolahan panas yang dilakukan di atas 2000F dapat menghasilkan peningkatan kandungan ferrit.

Seperti semua stainless steel duplex, 2205 rentan terhadap presipitasi fase intermetallic, biasanya disebut sebagai fase sigma.dengan curah hujan paling cepat terjadi pada sekitar 1600FOleh karena itu, adalah bijaksana untuk memiliki 2205 lulus tes untuk tidak adanya fase intermetallic, seperti yang dalam ASTM A 923.

------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------

Pengolahan
Membentuk dengan panas
Membentuk di bawah 600F dianjurkan setiap kali mungkin. Ketika pembentukan panas diperlukan, benda kerja harus dipanaskan secara merata dan dioperasikan dalam kisaran 1750 sampai 2250F.Paduan 2205 cukup lunak pada suhu ini dan mudah terbentukDi atas rentang ini, 2205 tunduk pada panas robek. segera di bawah rentang ini, austenit menjadi jauh lebih kuat daripada ferrit dan dapat menyebabkan retakan,bahaya khusus untuk tepi yang dinginDi bawah 1700F dapat terjadi pembentukan fase intermetallic cepat karena kombinasi suhu dan deformasi.harus diikuti dengan penggilingan larutan penuh pada suhu minimum 1900F dan pemadam cepat untuk mengembalikan keseimbangan fase, ketangguhan, dan ketahanan korosi; mengurangi tekanan tidak diperlukan atau dianjurkan; namun, jika harus dilakukan, bahan harus menerima penggilingan larutan penuh pada minimum 1900F,diikuti dengan pendinginan cepat atau pemadam air.

Pembentukan Dingin
Alloy 2205 mudah dipotong dan terbentuk dingin pada peralatan yang cocok untuk mengolah stainless steel.kekuatan yang jauh lebih tinggi daripada yang dibutuhkan untuk baja austenit untuk membentuk 2205Juga karena kekuatan yang tinggi, izin yang agak lebih besar harus dibuat untuk springback.

Pengolahan Panas
Paduan 2205 harus dipanaskan pada suhu minimum 1900F, diikuti dengan pendinginan cepat, idealnya dengan penekan air.Pengolahan penghilang stres pada suhu yang lebih rendah membawa risiko presipitasi fase intermetallic atau nonmetallic yang merugikan.

------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------

Kemampuan mesin
Dengan alat baja berkecepatan tinggi, 2205 dapat diolah dengan input dan kecepatan yang sama dengan paduan 316L. Ketika alat karbida digunakan,kecepatan pemotongan harus dikurangi sekitar 20% dibandingkan dengan kecepatan untuk Alloy 316LMesin yang kuat dan pemasangan alat dan bagian yang kaku sangat penting.

------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------

Pengelasan
Alloy 2205 memiliki kemampuan las yang baik. Tujuan dari pengelasan 2205 adalah agar logam las dan zona yang terkena panas (HAZ) mempertahankan ketahanan korosi, kekuatan, dan ketangguhan logam dasar.Pengelasan 2205 tidak sulit, tetapi perlu untuk merancang prosedur pengelasan yang mengarah pada keseimbangan fase yang menguntungkan setelah pengelasan dan akan menghindari presipitasi fase intermetallic atau nonmetallic yang merugikan.

2205 dapat dilas dengan: GTAW (TIG); GMAW (MIG); SMAW ("stick" electrode); SAW; FCW; dan PAW.

Jika Anda membutuhkan produk kami, silakan kirim email kepada kami.

5mm   100mm Duplex 2205 S32205 Plat Duplex Plat Baja S31803 2B 1D Permukaan 05mm   100mm Duplex 2205 S32205 Plat Duplex Plat Baja S31803 2B 1D Permukaan 15mm   100mm Duplex 2205 S32205 Plat Duplex Plat Baja S31803 2B 1D Permukaan 2

Rincian kontak
JIANGSU MITTEL STEEL INDUSTRIAL LIMITED

Kontak Person: Mr. Gao Ben

Tel: +86-18068357371

Faks: 86-0510-88680060

Mengirimkan permintaan Anda secara langsung kepada kami (0 / 3000)