SUS301 Stainless Steel Coils Kendali Keras AISI 301 Metal Strip 4 / 4H 2B Finish

Sertifikasi
CINA JIANGSU MITTEL STEEL INDUSTRIAL LIMITED Sertifikasi
CINA JIANGSU MITTEL STEEL INDUSTRIAL LIMITED Sertifikasi
Ulasan pelanggan
this is the second order l buy this company ,quality is very good ,same as europure quality .we will go on ccooperate with this company .

—— Andrew Greg - Turkey

200 ton Stainless steel sheet is arrived on 10th Oct 2014 , the quality is very good.,deliver time is very fast It's very lucky we find this factory

—— Mechile Kilar Chard - Brazial

We Have Cooperate With this Factory Many Years , Everything Goes Very Well.l Like This Factory !

—— Tony Hilton - Poland

This is Our Thrid Time Buy from Mittel,Quality is Very Goods ,We Are Glad to Find This Reliable Factory

—— Natalya Ugay-Russia

Quality is very good and delivery time very fast ,we want to do long terms business with this company

—— Pongpol Pluemsati-Thailand

I 'm Online Chat Now

SUS301 Stainless Steel Coils Kendali Keras AISI 301 Metal Strip 4 / 4H 2B Finish

SUS301 Stainless Steel Coils Kendali Keras AISI 301 Metal Strip 4 / 4H 2B Finish
SUS301 Stainless Steel Coils Kendali Keras AISI 301 Metal Strip 4 / 4H 2B Finish SUS301 Stainless Steel Coils Kendali Keras AISI 301 Metal Strip 4 / 4H 2B Finish

Gambar besar :  SUS301 Stainless Steel Coils Kendali Keras AISI 301 Metal Strip 4 / 4H 2B Finish

Detail produk:
Tempat asal: Cina
Nama merek: TISCO
Sertifikasi: SGS ISO
Nomor model: 301
Syarat-syarat pembayaran & pengiriman:
Kuantitas min Order: 1 TON
Harga: 2980 USD/Ton
Kemasan rincian: Ekspor Packing
Waktu pengiriman: 7 hari
Syarat-syarat pembayaran: 500 Ton
Menyediakan kemampuan: 500 Ton

SUS301 Stainless Steel Coils Kendali Keras AISI 301 Metal Strip 4 / 4H 2B Finish

Deskripsi
Ketebalan: 0.01-3.0mm Lebar: 12.7-2000mm
Permukaan: 2B BA 6K 8K Mengetik: Roleld Dingin
Kekerasan: 1 / 4H 1 / 2H 3 / 4H 4 / 4H
Cahaya Tinggi:

saham coil baja stainless

,

kumparan baja cold rolled

SUS301 Strip Stainless Steel Coil Full Hard AISI 301 Strip Logam 4 / 4H 2B Selesai

301 strip stainless, ASTMA-666, sedikit lebih rendah dalam kandungan kromium dan nikel daripada Tipe 302. Kandungan nikel yang lebih rendah menyebabkan Tipe 301 bekerja mengeras lebih cepat dan mempertahankan keuletan yang lebih besar daripada temperamen yang sama dari Tipe 302. Saham Gibbs 301 Stainless Strip di alat pengukur dari 0,0022 "ke 0,050" presisi celah untuk lebar dari 0,022 hingga 12 ". Tipe 301 tersedia dalam berbagai macam emosi.

Stainless Steel - Grade 301 (UNS S30100)

Topik Covered

pengantar
Properti Kunci
Komposisi
Peralatan mekanis
Properti fisik
Perbandingan Spesifikasi Kelas
Kemungkinan Nilai Alternatif
Tahan korosi
Tahan panas
Perawatan panas
Bekerja Dingin
Pengelasan
Aplikasi

Formula kimia

Fe, <0,15% C, 16-18% Cr, 6-8% Ni, <2% Mn, <1% Si, <0,045% P, <0,03% S

pengantar

Stainless steel grade 301 biasanya disediakan dalam bentuk strip dan kabel, dengan kekuatan tarik hingga 1800 Mpa, untuk menghasilkan temper mulai dari 1/16 Hard to Full Hard. Dengan menundukkan kelas 301 untuk analisis terkontrol, ia mampu mempertahankan keuletan yang cukup bahkan dalam ½ kondisi keras. Bentuk kelas 301 ini dapat digunakan dalam pesawat terbang, komponen kereta api mobil dan struktur arsitektur. Tempers grade ini, mulai dari ¾ hingga full hard, dapat digunakan dalam aplikasi yang memerlukan ketahanan aus yang tinggi dan fitur pegas dengan desain bentuk sederhana.

Grade 301L, yang merupakan bentuk karbon rendah kelas 301, adalah pilihan ideal untuk aplikasi yang memerlukan keuletan yang baik. Grade 301LN adalah varian lain. Ini mengandung persentase nitrogen yang lebih tinggi dan menunjukkan tingkat hardener kerja yang lebih tinggi dibandingkan dengan standar 301. Hanya tingkat 301 yang ditentukan dalam ASTM A666. 301L dan 301LN diwakili oleh konvensi lain. Grade 301L diwakili oleh JIS G4305 dan 301LN oleh EN10088-2 sebagai kelas 1.4318.

Properti Kunci

Properti utama yang tercantum dalam bagian di bawah ini adalah untuk produk canai lantai seperti pelat, lembaran dan kumparan - ditetapkan sebagai Grade ASTM A666. Untuk kelas lain, EN10088.2 dan JISG4305, tidak perlu bahwa nilai dan propertinya identik.

Komposisi

Komposisi rentang kelas stainless steel 301 ditabulasikan di bawah ini.

Tabel 1 - Komposisi rentang untuk stainless steel kelas 301

Kelas C M N Si P S Cr Mo Ni N

301

ASTM A666

mnt

maks.

-

0,15

-

2.0

-

1.0

-

0,045

-

0,030

16,0

18,0

-

6.0

8.0

-

0,10

301L

JIS G4305

mnt

maks.

-

0,03

-

2.0

-

1.0

-

0,045

-

0,030

16,0

18,0

-

6.0

8.0

-

0,20

1.4318 / 301LN

EN 10088-2

mnt

maks.

-

0,03

-

2.0

-

1.0

-

0,045

-

0,015

16,5

18,5

-

6.0

8.0

0,10

0,20

Peralatan mekanis

Sifat mekanik baja tahan karat kelas 301 tercantum dalam tabel di bawah ini. Uji tikungan diperoleh sekitar diameter faktor tikungan dikalikan dengan ketebalan baja.

Tabel 2 - Sifat mekanik dari baja stainless grade 301

Grade 301 Temper ASTM A666 Kekuatan Tarik (MPa) min. Kekuatan Hasil 0,2% Bukti (MPa) min. Elongasi (% dalam 50mm) (tebal.> 0,76mm) min. Bend Test (ketebalan> 1.27mm)
Tikungan sudut (°) Faktor
Anil 758 276 60 - -
1/16 Keras 620 310 40 180 1
1/8 Keras 690 380 40 180 1
1/4 Keras 862 514 25 90 2
1/2 Keras 1034 758 18 90 2
3/4 Keras 1205 930 12 90 3
Keras Penuh 1276 965 9 90 5

Properti fisik

Sifat fisik baja tahan karat kelas 301 tercantum dalam tabel di bawah ini.

Tabel 3 - Sifat fisik dari stainless steel kelas 301

Kelas Kepadatan (kg / m 3 ) Modulus Elastis (GPa) Mean Coefficient of Thermal Expansion (μm / m / ° C) Konduktivitas Termal (W / mK) Panas Khusus 0-100 ° C
(J / kg.K)
Resistivitas Listrik (nΩ.m)
0-100 ° C 0-315 ° C 0-538 ° C pada 100 ° C pada 500 ° C
301 7880 193 16,9 17.2 18.2 16.2 21,4 500 695

Perbandingan Spesifikasi Kelas

Tabel 4 memberikan perbandingan nilai perkiraan untuk 301 baja tahan karat. Perbandingan yang diberikan dalam tabel adalah bahan-bahan fungsional yang serupa. (Untuk ekuivalen yang tepat, spesifikasi asli harus dirujuk).

Tabel 4 - Perbandingan kelas untuk stainless steel kelas 301

Kelas UNS No Inggris Kuno Euronorm SS Swedia JIS Jepang
BS En Tidak Nama
301 S30100 301S21 - 1,4310 X10CrNi18-8 2331 SUS 301

Kemungkinan Nilai Alternatif

Daftar alternatif yang mungkin untuk grade 301 stainless steel diberikan pada Tabel 5.

Tabel 5 - Kemungkinan nilai alternatif untuk stainless steel kelas 301

Kelas Alasan memilih kelas pengganti
304 Tingkat pengerasan kerja yang lebih rendah dari 304 dapat diterima, memberikan keuletan yang lebih baik diperlukan untuk membentuk.
316 Ketahanan korosi yang lebih tinggi diperlukan, dan tingkat pengerasan kerja yang lebih rendah dari 316 dapat dikompensasikan.

Tahan korosi

Ketahanan terhadap korosi yang ditawarkan oleh stainless steel kelas 301 mirip dengan yang ditawarkan oleh 304. Kelas ini menunjukkan ketahanan yang baik terhadap korosi dalam lingkungan korosif ringan pada suhu kamar.

Tahan panas

Grade 301 menunjukkan ketahanan oksidasi yang baik untuk layanan intermiten hingga 840 ° C dan untuk layanan berkelanjutan hingga 900 ° C.

Perawatan panas

Stainless steel kelas 301 dikenakan solusi pengobatan anil dalam suhu mulai dari 1010oC hingga 1120 ° C diikuti oleh pendinginan cepat. Untuk anil menengah, kisaran suhu rendah dipilih. Pengerasan termal tidak sesuai dengan grade baja tahan karat ini.

Bekerja Dingin

Stainless steel kelas 301 dan varian karbon rendah dari kelas ini sebagian besar digunakan sebagai baja tahan karat berkekuatan tinggi. Tingkat pengerasan kerja untuk grade ini sangat tinggi, dalam kisaran peningkatan 14 MPa per pengurangan 1% di area kerja dingin. Sebagai hasil dari kekuatan tinggi karakteristik ini dapat dicapai dari operasi cold rolling dan roll forming.

Melalui metode pembentukan seperti itu, regangan austenit yang mengeras dapat diubah sebagian menjadi martensit. Meskipun mencapai kekuatan tinggi seperti itu, keuletan sisa dalam paduan mampu menyebabkan deformasi dingin yang parah. Paduan ini non-magnetik dalam kondisi anil, tetapi menunjukkan magnet yang kuat ketika dingin bekerja.

Pengelasan

Stainless steel kelas 301 cocok untuk semua bentuk metode pengelasan standar. Penggunaan kelas 308L sebagai pengisi logam dianjurkan. Bagian yang dilas di kelas 301 harus dikenai pelunakan untuk mendapatkan ketahanan korosi maksimum. Untuk nilai 301L dan 301LN annealing tidak diperlukan setelah pengelasan. Tujuan pengelasan diikuti oleh annealing adalah untuk menghilangkan kekuatan tinggi yang dibawa oleh cold rolling.

Proses pengelasan spot digunakan untuk merakit komponen canai dingin 301; teknik pengelasan cepat ini tidak menghambat kekuatan keseluruhan komponen.

Aplikasi

Beberapa aplikasi khas baja tahan karat kelas 301 tercantum di bawah ini:

  • Pembuatan komponen struktural kereta api mobil
  • Bagian bingkai udara
  • Komponen trailer jalan raya
  • Penutup roda otomotif
  • Klip dan pemegang pisau penghapus
  • Jepit elemen kompor
  • Bingkai layar
  • Pemanggang roti
  • Dinding tirai

Rincian kontak
JIANGSU MITTEL STEEL INDUSTRIAL LIMITED

Kontak Person: Mr. Gao Ben

Tel: +86-18068357371

Faks: 86-0510-88680060

Mengirimkan permintaan Anda secara langsung kepada kami (0 / 3000)