S31803 S32205 Pelat Baja Stainless Hot Rolled 0.5 - 20mm Tebal

Sertifikasi
kualitas baik pelat baja stainless untuk penjualan
kualitas baik pelat baja stainless untuk penjualan
Ulasan pelanggan
this is the second order l buy this company ,quality is very good ,same as europure quality .we will go on ccooperate with this company .

—— Andrew Greg - Turkey

200 ton Stainless steel sheet is arrived on 10th Oct 2014 , the quality is very good.,deliver time is very fast It's very lucky we find this factory

—— Mechile Kilar Chard - Brazial

We Have Cooperate With this Factory Many Years , Everything Goes Very Well.l Like This Factory !

—— Tony Hilton - Poland

This is Our Thrid Time Buy from Mittel,Quality is Very Goods ,We Are Glad to Find This Reliable Factory

—— Natalya Ugay-Russia

Quality is very good and delivery time very fast ,we want to do long terms business with this company

—— Pongpol Pluemsati-Thailand

I 'm Online Chat Now

S31803 S32205 Pelat Baja Stainless Hot Rolled 0.5 - 20mm Tebal

Cina S31803 S32205 Pelat Baja Stainless Hot Rolled 0.5 - 20mm Tebal pemasok
S31803 S32205 Pelat Baja Stainless Hot Rolled 0.5 - 20mm Tebal pemasok S31803 S32205 Pelat Baja Stainless Hot Rolled 0.5 - 20mm Tebal pemasok

Gambar besar :  S31803 S32205 Pelat Baja Stainless Hot Rolled 0.5 - 20mm Tebal

Detail produk:

Tempat asal: Cina
Nama merek: TISCO ,ZPSS,BAO STEEL
Sertifikasi: SGS ISO
Model Number: S31803 S32205

Syarat-syarat pembayaran & pengiriman:

Kuantitas min Order: 5 ton
Harga: 3450 USD/Ton
Packaging Details: Export Packing
Supply Ability: 500 tons
Contact Now
Detil Deskripsi produk
Lebar: 1000-2000mm Panjang: 2000-6000mm
Permukaan: 2B NO.1 Ketebalan: 0.5-20mm
Jenis: Hot Rolled

S32205 Duplex Steel Plate S31803 Duplex Material Stainless Steel

1.4462 Lembar dan Pelat

Baja tahan karat dupleks sangat tahan korosi, paduannya bisa dikeraskan. Mikrostrukturnya terdiri dari campuran fase austenit dan ferit. Akibatnya, karakteristik baja dupleks duplex menampilkan sifat karakteristik baja tahan karat austenitik dan feritik. Kombinasi sifat ini bisa berarti beberapa kompromi bila dibandingkan dengan nilai feritik austenitik murni dan murni.
Duplex baja tahan karat dalam banyak kasus, lebih keras daripada baja tahan karat feritik. Kekuatan baja tahan karat dupleks dapat dalam beberapa kasus menjadi dua kali lipat untuk baja tahan karat austenitik.
Sementara baja tahan karat dupleks dianggap tahan terhadap korosi retak, mereka tidak tahan terhadap bentuk serangan ini sebagai baja tahan karat feritik. Namun, ketahanan korosi pada baja tahan karat dupleks yang paling tidak tahan lebih besar dari pada nilai baja tahan karat yang paling umum digunakan, yaitu 304 dan 316.
Baja dupleks juga magnetis, properti yang dapat digunakan untuk membedakannya dengan mudah dari nilai austenitik karat yang umum.
Data properti yang diberikan dalam dokumen ini khas untuk produk canai rata yang tercakup dalam EN 10088-2: 2005. ASTM, EN atau standar lainnya mungkin mencakup produk yang dijual. Adalah wajar untuk mengharapkan spesifikasi dalam standar ini serupa tetapi tidak harus identik dengan yang diberikan dalam datasheet ini.

Komposisi kimia

Spec: EN 10088-2: 2005

1.4462 Baja

Elemen Kimia % Hadir
Karbon (C) 0,0 - 0,03
Chromium (Cr) 21.00 - 23.00
Mangan (Mn) 0,0 - 2.00
Silikon (Si) 0,0 - 1.00
Fosfor (P) 0,0 - 0,03
Sulfur (S) 0,0 - 0,02
Nikel (Ni) 4.50 - 6.50
Nitrogen (N) 0,10 - 0,22
Molybdenum (Mo) 2,50 - 3,50
Besi (Fe) Keseimbangan

roperties

Sifat fisik Nilai
Massa jenis 7.805 g / cm³
Ekspansi termal 13,7 x10 ^ -6 / K
Modulus Elastisitas 200 GPa
Konduktivitas termal 19.0 W / mK
Resistivitas Listrik 0,085 x10 ^ -6 Ω .m

Spec: EN 10088-2: 2005

Lembaran - Sampai 8mm tebal

Properti mekanik Nilai
Bukti Stres 500 Min MPa
Daya tarik 700 sampai 950 MPa
Pemanjangan A50 mm 20 Min%

Spec: EN 10088-2: 2005

Piring - lebih dari 8mm sampai 13.5mm Tebal

Properti mekanik Nilai
Bukti Stres 460 Min MPa
Daya tarik 700 sampai 950 MPa
Pemanjangan A50 mm 25 Min%

Spec: EN 10088-2: 2005

Piring - Lebih dari 13.5mm sampai 75mm Tebal

Properti mekanik Nilai
Bukti Stres 460 Min MPa
Daya tarik 640 sampai 840 MPa
Pemanjangan A50 mm 25 Min%

Penunjukan Paduan

Kelas 1.4462 / 2205 mirip tapi mungkin tidak setara langsung:

UNS S31803

UNS S32205

BS 318S13


Formulir yang Disediakan

  • Fittings & Flensa
  • Pipa
  • Piring
  • Lembar
  • Tabung
  • Bar

Aplikasi

Baja stainless dupleks biasanya digunakan dalam:

~ Pengolahan kimia, transportasi dan penyimpanan

~ Eksplorasi minyak dan gas dan rig lepas pantai

~ Minyak dan gas penyulingan

~ Lingkungan laut

~ Peralatan kontrol polusi

~ Pulp & manufaktur kertas

~ Pabrik proses kimia


Tahan korosi

Baja tahan karat dupleks sangat tahan korosi. Mereka memiliki ketahanan tinggi terhadap korosi intergranular. Bahkan di lingkungan klorida dan sulfida, baja tahan karat dupleks menunjukkan ketahanan yang sangat tinggi terhadap retak korosi tegangan.

Nilai super duplex bahkan lebih tahan terhadap korosi.


Perlawanan panas

Kandungan kromium tinggi dari baja tahan karat dupleks yang melindungi dari korosi, menyebabkan embrittlement pada suhu di atas sekitar 300 ° C.

Pada suhu rendah, baja tahan karat dupleks memiliki daktilitas yang lebih baik daripada nilai feritik dan martensit. Nilai dupleks dapat dengan mudah digunakan paling sedikit -50 ° C.


Pembuatan

Fabrikasi semua baja tahan karat harus dilakukan hanya dengan alat yang didedikasikan untuk bahan stainless steel. Perkakas dan permukaan kerja harus dibersihkan terlebih dahulu sebelum digunakan. Tindakan pencegahan ini diperlukan untuk menghindari kontaminasi silang baja tahan karat dengan logam berkarat mudah yang dapat mengubah permukaan produk yang dipalsukan.


Machinability

Meski bisa digunakan, kekuatan baja dupleks tahan karat yang tinggi membuat mesin menjadi sulit. Sebagai contoh, mesin 2205 sekitar 20% lebih lambat dari pada 304.

Machining dapat ditingkatkan dengan menggunakan aturan berikut:

~ Cutting edge harus dijaga tetap tajam. Tepi kusam menyebabkan pengerasan kerja berlebih.

~ Potongan harus ringan tapi cukup dalam untuk mencegah pengerasan kerja dengan mengendarai di permukaan material.

~ Chip breaker harus digunakan untuk membantu memastikan swarf tetap bersih dari pekerjaan

~ Konduktivitas termal rendah paduan austenitik menghasilkan panas yang terkonsentrasi pada tepi pemotongan. Ini berarti pendingin dan pelumas diperlukan dan harus digunakan dalam jumlah banyak.


Perawatan panas

Baja tahan karat dupleks tidak bisa dikeraskan dengan perlakuan panas. Namun mereka bisa bekerja keras.

Pengobatan atau annealing solusi dapat dilakukan dengan pendinginan cepat setelah pemanasan sampai sekitar 1100 ° C.


Weldability

Baja tahan karat dupleks memiliki kemampuan las yang bagus. Semua proses pengelasan standar bisa digunakan. Mereka tidak mudah dilas seperti nilai austenitik namun ekspansi termal rendah pada nilai dupleks mengurangi distorsi dan tegangan sisa setelah pengelasan. Bahan pengisi yang direkomendasikan untuk 2205 stainless steel adalah 2209.